APPLICATION:
A product specially formulated for primary coating various porous
and adsorbent surfaces. It has high penetration and strengthening
properties, and provides good humidity protection. It can be
used on various mineral surfaces, such as: cement and lime cement
plasters, cement sheets, concrete, aerated concrete, natural
stone, fences, foundations. It is waterproof and does not change
the structure or look of the above materials.
TIEF PRIMER-H can also be used under paint, acrylic and mineral
plaster, plasterboards, glue paint, joint less floors, self-levelling
floors, tiles, etc.
Note:
Do not use active primer when a bonding primer is required
Priming surfaces that are too "fresh", unseasoned
plaster or other surfaces (with unbalanced air/surface humidity)
are liable to "burn-outs".
PREPARING SURFACES & USAGE:
Surfaces should be clean and free of dirt and grease. With
very absorptive surfaces and thick layers requiring strengthening
the best priming method is applying the primer using the "wet-on-wet"
technique, which will ensure deep enough penetration of the
substrate. In this circumstance it is necessary to dilute
the primer with drinking water in a ratio 1:1. More water
is required when the temperature exceeds 30°C or when
working on a warm surface. With less absorptive surfaces it
is possible to dilute with water or use undiluted.
It can be applied with various tools such as brush, roller
or spray, depending on the absorption of the surface and porosity.
A test should be performed on a few square metres to estimate
the number of layers and consistency required.
1 to 3 layers are recommended. Subsequent layers can be applied
after 2 hrs.
Please bare in mind the following:
An over-primed surface will cause paint smearing on the primed
layer (looking up towards the light the surface reflects light
like glass). To cure this problem, dilute the paint until
it is of sufficient consistency to "catch" on the
over-primed surface.
The absorptive quality of the surface should be directly compared
using sprayed water droplets with a sample of low absorptive
material (e.g. plasterboard) until such time as they are similar.
Highly absorptive surfaces greatly reduce the efficiency of
paint, and thus increase costs.
After drying the coating is transparent, waterproof and vapour-permeable.
EFFICIENCY:
Average total usage depends totally on the reason the primer
is being used. For very absorptive surfaces it could be 0.15
-0.22 l/m2. For strengthening and regulating the absorption
for surfaces with medium absorption the usage will be 0.08-0.14
l/m2. For new surfaces where we are balancing the absorption
between different materials (e.g. plasterboard and joining
materials), usage will be close to 0.05 l/m2.
STORAGE, USE AND TRANSPORT:
TIEF PRIMER-H should be stored, used and transported in its
originally closed packaging at a temperature of +5° -
+35°C (also includes surface temperature) and in clean
dry conditions. Protect from frost.
BEST BEFORE:
2 years from date of production.